A sure-fire way to make any injection mold toolmaker or processing engineer uneasy is to utter the words “fibre reinforced”; and not without good reason.
Fibre reinforced polymer materials have seen a constant increase in uptake across all industries. Their benefits are substantial; with the fibres providing superior strength, stiffness and creep resistance over conventional unfilled polymers. These outstanding properties make these materials attractive alternatives to metal in many applications.
All this is fantastic news for product designers, but achieving exacting dimensional tolerances can be a real headache for those responsible for manufacturing these components.
At the root of the problem is shrinkage. All thermoplastics shrink during manufacture and this shrinkage is compensated for by making the mold tool slightly larger than the desired part. The fibres distributed within the polymer matrix resist this shrinkage, but the extent of this effect depends on the fibre direction.
During filling the fibres are aligned by the shear forces within the melt flow, which tend to align fibres in the flow direction. The sample plaque below shows a typical fibre orientation, resulting in low shrinkage in the flow direction.
![Shrinkage variation in a fibre reinforced sample plaque figure-1-shrinkage-variation](https://wilde.pdsvision.online.hemsida.eu/wp-content/uploads/2017/02/Figure-1-Shrinkage-variation-1024x326.png)
The problem is exaggerated for materials with very high fibre filler content. It’s not unusual to see transverse shrinkage 5-10x higher than parallel.
Take this clam shell handle from a garden tool as an example. A 33% glass fibre reinforced nylon material was specified by the designer to ensure sufficient strength and stiffness. When the first parts came off the injection molding machine there were complaints of poor fit when assembled.
By running a quick Moldex3D analysis on the part the cause of the problem becomes clear. As the polymer reaches the end of the part the flow front converges on the end face. The resulting radial alignment of the fibres causes a high spot on the mating face.
In Moldex3D, the warped shape can now be exported as a modified ýapp geometry file. Then it’s just a case of dropping the warped model back into the ýapp assembly to assess fit and function..
![Comparison of actual part and Moldflow prediction figure-4-comparison-of-actual-part-and-moldflow-prediction](https://wilde.pdsvision.online.hemsida.eu/wp-content/uploads/2017/02/figure-6-comparison-of-actual-part-and-Moldflow-prediction.png)
![Comparison of gate positions figure-8-comparison-of-gate-positions](https://wilde.pdsvision.online.hemsida.eu/wp-content/uploads/2017/02/Figure-8-comparison-og-gate-positions-183x300.png)
Many distortion issues can be mitigated by careful control of the molding process but distortion due to fibre orientation effects is often the exception. Gate position is single biggest factor in achieving good part quality. For the handle component Moldex3D analysis shows us that gating close to the end face minimises the distortion issues.
By taking the ýapp model into a visualization package like Keyshot it’s easy to assess the improvement.
Louis Barnes, Principal Engineer